Cristal SLN para sierra de alta temperatura

Ventajas de MgO:SLN
Bajo campo magnético: adecuado para procesos de coincidencia de fase de alta precisión y alta velocidad
20%-50% mayor conductividad térmica mayor que el MgO:LN normal
Alto umbral de daño fotorrefractivo


  Contactar ahora
Detalles del producto

Nominally pure stoichiometric LiNbO 3 " rol="presentación"> LiNbO 3 shows lower photorefractive damage resistance than congruent crystal; however, stoichiometric crystals doped with MgO of more than 1.8 mol. % exhibit no measurable photorefractive damage at 532 nm to intensities of as much as 8 megavatios / cm 2 " rol="presentación"> 8   Mw / cm 2 . This remarkable damage resistance can be attributed not only to increased photoconductivity but also to decreased photogalvanic current. Stoichiometric magnesio : LiNbO 3 " rol="presentación"> Mg : LiNbO 3 also demonstrates the shortest absorption edge, 302 nm, and a single-domain nature with low scattering losses.


Aplicaciones Típicas
Dispositivo periódicamente polarizado
dispositivo de THz


Descripción

Valor

Borde de absorción (20 cm -1 )

303 ( c =49,9)

Índice de birrefringencia (633nm)

-0.0900 ( c =50.0)

Coeficiente electroóptico (pm/V)

R 61 = 9,89 ( c = 49,95)

Coeficiente no lineal (pm/V)

17,5 ( c =49,8)

Pico de absorción de OH/FWHM(cm -1

3465,5/2,9 ( c =49,9)

Voltaje de inversión de dominio (kV/cm²)

0,8 ( c =49,9)

Umbral de daño

100MW/ cm2 @532nm

c en la tabla es el contenido de Li 2 O del cristal




SLN Crystal for High Temperature SAW.jpg


SLN Crystal for High Temperature SAW.jpg


SLN Crystal for High Temperature SAW.jpg